Dental Laboratory Materials Translucent Zirconia YUCERA Zirconia Block
Natural Color Transition
zirconia blocksare made of nanometer medical grade zirconia powder. The powder are firstly compacted by cold isostaticpressing with high compressive strength and then pre-sintered to a certain degree to offer good machinability.
HT zirconia blocks can be used to create crowns, bridges, inlays and veneers of fixed partial denture with different translucency levels and colors.
High 1200MPA Translucent Zirconia Blocks Advantages:
1, Excellent translucency
2, High flexural strength
3,Accurate shading when working with our color liquid
4, Good machinability
5, Extremely safe
HT/ST Sintering Curve (1-5)
| HT/ST Sintering Curve (1-5) |
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 300 | 30 | 9.3 |
| Step 2 | 300 | 1200 | 150 | 6 |
| Step 3 | 1200 | 1530 | 110 | 3 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 100 | -7.3 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
HT/ST Sintering Curve (10 units)
| HT/ST Sintering Curve (10 units) |
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 300 | 30 | 9.3 |
| Step 2 | 300 | 1200 | 190 | 4.7 |
| Step 3 | 1200 | 1530 | 150 | 2.2 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 120 | -6 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
HT Zirconia Block
* High translucent
* Brilliant bending strength and economic block
* Suitable for coping and framework
Indications: Coping, Inlay, Onlay, Bridge, Crown
| Physical Characteristics |
| Sintered density 6.07±0.01g/cm³ |
| Bending Strength 1200 MPa |
| Transmittance 41% |
| Hardness 1200HV |
| Sintering temperature 1480~1550℃/recommend 1530℃ |
Product Tags:
|
|
HT 98x10mm 1200MPA Translucent Zirconia Blocks For Dental Lab Images
|